Hello everyone -

It is my understanding that a surface charge forms on a substrate after
specific processes.  For example, etching soda lime glass using BOE 6:1 or
10:1.  Is this true?  More importantly - if a surface charge does form - do
the high temperatures used in thermal bonding affect it?  Your experience
and any references are greatly appreciated.

Regards.