Can not understand what is "wrinkling": do you mean the working side (that was
in contact with master chip) did not repeat the features of master mold?

Was the pdms hardened totally or not?

What is antistick layer? If it contains mercaptane, or chlorine, or cyane - it
can be a reason of non-hardened pdms.