Hi Kim,
if you are not interested to have perpendicular walls you can use
isotropic etch (HNA). You will have a meniscus-like shape.

Best regards,
Andrea

> Hi
> Is it possible to make circular grooves (about 50 um deep) in {100}-Si by
> wet etching.
>
> Any suggestion will be highly appreciated.
>
> Best regards
> Kim